PLATING RESIST MR-303F油墨

PLATING RESIST MR-303F是适合用于部分镀金用的遮蔽的单液性, 碱性剥离型抗镀油墨.此外也适合用于ITO用的蚀刻油墨.

 
PLATING RESIST MR-303F is one component, alkaline removable type Resist Ink developed for masking of partial Au plating.
Moreover, it is possible to be used as etching ink for ITO.

Main Feature
1. Cured film has flexibility, and available for a flexible board and a rigid board.
2. This ink has excellent resistance to Au plating( Electro-less),since the contamination to the plating solution
is very small, control of the solution is easy.
3. Possible to be used as etching ink for ITO.

Main Property

Items Representing value Remarks
Color Black color Visual
Viscosity at 25 deg.C 200 dPa・s Viscotester VT-04
Applicable Screen 150~250 Mesh Polyester Screen
Optimum Ink thickness after drying 10~20µm Thickness Meter
Dry Conditions 100deg.C × 10min Circulating Heat Oven
Adhesion 100 / 100 Cross-cut,tape peel test
Resistance to Electro-less Plating No penetration, No color change Ni Plating at 90deg.C for 30 min + Au Plating at 90deg.C for 40 min
Remove of the cured film 1~3 wt% NaOH Solution 30deg.C × 1~3 min Dipping

The above information obtained by actual measurement at our lab., and do not specified values.
< Shelf-life > Main body: 6 months --- Stored in 25 deg.C or below (cool and dark place).
Usage and handling precautions
1. If dilution is needed due to viscosity variation during operation, dilute with exclusive reducer #70 within 5%.
2. Drying should be done at the range of 100deg.C~130deg.C. Since drying time will vary based on s heat efficiency and ventilation capacity of used oven, please confirm your oven and set optimum condition.
3. This resist can be used for general Ni/Au plating solution without any inconvenience.

However, if it is used for special plating solution, it may cause the change in characteristics, depending on its composition. Please use it after checking fully.

Flexibility test (JIS K 5600-5-1)

Mandrel diameter 8mmφ 6mmφ 4mmφ 3mmφ 2mmφ
Conventional products No Crack Crack Crack Crack Crack
MR-303F No Crack No Crack No Crack No Crack No Crack

Test board: Thickness 25µm/PI film
Screen mesh: 200mesh polyester screen
Dry condition: 100deg.C × 10min Circulating Heat Oven
Ink thickness after drying: Thickness 14~16µm

Elusion amount in Electro-less Ni Plating 

 

 ・Absorbance is high=Quantity of elution is large ・Absorbance is low=Quantity of elution is small Compared to Ni Plating new solution, absorbance peak which arise from elusion content from coated film can be confirmed at around 280nm for conventional product though, the peak can not be confirmed in MR-303F.

<<Sample manufacture condition>>
Test Board: 5.6cm×4cm /PI film/4 pieces
Dry condition: 100deg.C × 10min Circulating Heat Oven
Ink thickness after drying: About 30µm
<<Ni plating condition>>
Plating solution: Product made by OKUNO CHEMICAL INDUSTRIES CO.,LTD
Dip condition: 80 deg.C × 4hr
<<Measurement condition>>
Testing equipment: Product made in SHIMADZU CORPORATION UV-1800
Kind of measurements: Absorbance
Measurement wavelength(nm): 200~900

ITO-proof etching liquid test 

<<Sample manufacture condition>>
Test Board: ITO/PET film
Screen mesh: 200mesh polyester screen
Dry condition: 100deg.C × 10min Circulating Heat Oven
Ink thickness after drying: Thickness 10~15µm

≪ITO etching liquid condition≫
Etching solution: Mixed acid ITO-02 Product made by KANTO CHEMICAL CO.,INC.
Dip condition: 45deg.C × 4min
 ≪Remove of the cured film≫
Remove solution: 3wt%NaOH
Dip condition: 30 deg.C × 1min
≪Measuring instrument condition≫
Measuring instrument Product made by YOKOGAWA ELECTRIC CORPORATION DEGITAL MLTIMETER 755S

Stripping test after thermal resistance 


<<Sample manufacture condition>>
Test Board: PI film・ Glass epoxy copper foil
Screen mesh: 200mesh polyester screen
Dry condition: 100deg.C × 10min Circulating Heat Oven
Ink thickness after drying: Thickness 10~15µm
Additional heating condition: 180℃×1-5hr/ Heat circulation oven
≪Remove of the cured film≫
Remove solution: 3wt%NaOH
Dip condition: 30 deg.C × 1min
Check strippability: Visual

 

CST (Asia) Limited  电话: 深圳: 0755-2308 6405 苏州: 0512-52821513 香港: 00852-2602-6173
地址:香港新界沙田火炭穗禾路1号丰利工业中心4字楼13室  在线QQ:  893008608
Copyright(C) www.a1c81.cn All rights reserved   技术支持:湖北快三遗漏   电话:13183843395
名站导航: 湖北快三遗漏 | 触摸屏B2B | 触摸屏论坛 | 触摸屏人才 | 湖北快三遗漏


客服:
  • 三星Gear S4智能手表曝料:支持LTE 金色配色三星GearS4智能手表曝料-手机行情 2018-10-24
  • 因涉嫌违规 庞大集团遭证监会立案调查 2018-10-24
  • 天津自贸试验区天津港东疆片区:策源地的奔跑者 2018-07-14
  • 文代会、作代会系列访谈第二场 2018-07-14
  • 言而无信似乎成了特朗普政府的特质与标致 2018-07-13
  • 逾8成受访者担心使用照片特效程序会泄露个人信息 2018-07-13
  • 南宁市开展普法宣传进校园活动 2018-07-12
  • 最暖心的约定!清华给落选者发出一封这样的信…… 2018-07-12
  • 农民曲艺家刘士福:方言土语讲述老百姓自己的故事 2018-07-12
  • 甘肃警方破获一起“微信卖茶叶”特大新型网络诈骗案 2018-07-12
  • 前5个月我国外贸进出口同比增8.8% 民企所占比重提升 2018-07-11
  • 展开心中之爱 公益之路福彩与您并肩同行 2018-07-11
  • 国家哲学社会科学成果文库 2018-07-10
  • 市场经济优胜劣汰,被淘汰的如房地产,造成了资源浪费。 2018-07-10
  • 三晋史话:发生在山西境内的那些上古神话故事 2018-07-10
  • 851| 774| 548| 140| 868| 177| 464| 420| 540| 825|